TiO_2/SiO_2TiO2/SiO2
1.TiO_2/SiO_2 were prepared by the chemical modification reaction on SiO_2, then the supported coupled semiconductors WO_3-TiO_2/SiO_2 were prepared by impregnating TiO_2/SiO_2.以表面改性法制备出TiO2/SiO2,进而以浸渍法制备出负载型复合半导体材料WO3-TiO2/SiO2,利用XRD、BET、TPR、UVDRS、IR和TPD等技术对材料的表面性质与构造、光响应性能和化学吸附性能进行了表征,并研究了该材料光催化甲烷和水合成甲醇和氢的反应性能。
2.The TiO_2/SiO_2 mixed oxides with high TiO_2 contents were prepared by the co-precipition method and characterized by means of BET、 XRD、 FT-IR and butylamine adsorption techniques, effect of calcination temperature on surface acidity of TiO_2/SiO_2 was studied.采用共沉淀法制备了高钛含量的复合氧化物TiO2/SiO2。
3)TiO 2/SiO 2TiO2/SiO2
1.Sn-modified TS-1 and TiO 2/SiO 2 showed preferable activity and selectivity.实验结果表明,Sn改性的TS-1分子筛、TiO2/SiO2对该反应具有较高的催化活性和选择性,前者DMO的转化率和目的产物的选择性分别可以达到50 3%和99 2%;后者分别为66 7%和99 5%。
4)TiO_2-SiO_2 solTiO2-SiO2溶胶
5)TiO2/CoFe2O4TiO2/SiO2/CoFe2O4
1.In the full paper, we present our experimental results on core-shell magnetic TiO2/SiO2/CoFe2O4 and TiO2/CoFe2O4 photocatalysts using spinel CoFe2O4 as core.文章以CoFe2O4纳米颗粒为核,研究了制备核壳型TiO2/CoFe2O4和TiO2/SiO2/CoFe2O4光催化剂的适宜工艺;用XRD和TEM分析了产物的结构组成与形貌;以TNT为目标降解物考察了催化剂的活性。
6)TiO_2-SiO_2/SO~(2-)_4TiO2-SiO2/SO24-
延伸阅读
CaO-TiO2-SiO2 ceramics分子式：CAS号：性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。