intergranular crack沿晶开裂
1.The reinforced connector of the down tail tube in hydrogen manufacturing converted furnace was intergranular crack.制氢转化炉下尾管加强接头发生沿晶开裂,对接头的化学成分、断口形貌、显微组织等进行了检测与分析。
2.Along with the diversification of components,the propagation form of cracks changes from intergranular crack into transcry.Ti/Al2O3界面处生成的Ti3Al相以及Ti3Al周围的气孔是热疲劳裂纹的主要萌生和扩展地;随着成分的变化,裂纹的扩展由沿晶开裂转变为穿晶断裂,裂纹扩展的路线并不是直线,在各梯度层间发生了裂纹的偏转。
3.The reinforced connector of the down tail tube in hydrogen manufacturing converted furnace was intergranular crack.制氢转化炉下尾管加强接头发生沿晶开裂,对接头的化学成分、断口形貌、显微组织等进行了检测与分析。
3)intergranular cracking沿晶开裂
1.The results show that the main reason for the cracking was high temperature intergranular oxidation,with the fracture morphology being a typical intergranular cracking character.结果表明,造成主蒸汽滤网开裂的主要原因是晶界高温氧化,断口呈典型的沿晶开裂特征。
4)grain boundary separation晶界开裂
5)intergranular cracking晶间开裂
6)transgranular cracking穿晶开裂