1)"point-seed" method"点籽晶"法
2)point seed点状籽晶
1.DKDP crystals were grown by the Z cut point seed (5mm×5mm×3mm) on the basis of the study on the stability of DKDP solution.本文在研究DKDP溶液稳定性的基础上 ,采用Z切点状籽晶 (5mm× 5mm× 3mm)生长了多块DKDP晶体 ,在2 5 0ml和 10 0 0ml生长瓶中分别获得了在 [10 0 ]和 [0 0 1]向生长速度可达到 3mm/d和 4 5mm/d的点状籽晶生长优质DKDP晶体的生长条件。
英文短句/例句
1.Growth of ADP point-seed crystal (100) surfaceADP点状籽晶(100)面的生长
2.The Study on Growth and Characterization of High Quality DKDP Crystal by Point Seed;点状籽晶生长优质DKDP晶体及其表征的研究
3.Growth and performance characterization of K_(1-x)(NH_4)_xH_2PO_4 mixed crystals grown onto point seedsK_(1-x)(NH_4)_xH_2PO_4混晶的点状籽晶法生长与性能表征
4.Rapid Growth and Properties Characterization of Middle Scale KDP Single Crystal“点籽晶”法快速生长中等口径KDP单晶及其性能表征
5.Study on the growth habit and optical property of DKDP crystal grown by different seed不同籽晶DKDP晶体生长和光学性能研究
6.Insetting Multi-seeds for YBCO Single Domain Depth Growth复层籽晶制备单晶畴YBCO超导块材
7.Clinical application of AcrySof Restor muitifocal intraocular lens.AcrySof ReStor多焦点人工晶状体的临床应用
8.Clinical Application of ACRYSOF ReSTOR Multifocal lntraocular Lens多焦点人工晶状体ACRYSOF ReSTOR的临床应用
9.Effects of grape seed proanthocyanidin extract on the growth and cell cycle of bovine lens epithelial cells in vitro葡萄籽原花青素提取物对牛晶状体上皮细胞增殖及细胞周期的影响
10.The kidney-shaped seed of this tree, eaten after roasting.贾如树籽这种树的肾状种籽，烤后可食
11.TiAl Seed Preparation & Fully Lamellar Structure Control Through Seeding and Directional Solidification;TiAl籽晶制备及定向全片层组织的研究
12.Observation the Result of Implantation of Array Multifocal Intraocular Lens;Array多焦点人工晶状体植入术后临床观察
13.Comparison of Three Different Multifocal IOLs;三种多焦点人工晶状体术后视觉质量的比较
14.A Study on Long Term Contrast Sensitivity of Multifocal Intraocular Lens Implantation.;多焦点人工晶状体术后远期对比敏感度的研究
15.Clinical Study on Application of a Multifocal Apodized Diffractive Intraocular Lens(Acrys of ReSTOR);Acrysof ReSTOR多焦点人工晶状体应用的临床研究
16.Application of diffractive multifocal IOL衍射型多焦点人工晶状体临床应用新进展
17.Early clinical application of RESTOR multifocal intraocular lens implantationReESTOR多焦点人工晶状体临床应用的初步报告
18.Clarify some problems when selecting multifocal intraocular lens应用多焦点人工晶状体应注意的一些问题
相关短句/例句
point seed点状籽晶
1.DKDP crystals were grown by the Z cut point seed (5mm×5mm×3mm) on the basis of the study on the stability of DKDP solution.本文在研究DKDP溶液稳定性的基础上 ,采用Z切点状籽晶 (5mm× 5mm× 3mm)生长了多块DKDP晶体 ,在2 5 0ml和 10 0 0ml生长瓶中分别获得了在 [10 0 ]和 [0 0 1]向生长速度可达到 3mm/d和 4 5mm/d的点状籽晶生长优质DKDP晶体的生长条件。
3)point-seed rapid growth method"点籽晶"快速生长法
4)seed technique籽晶法
5)TSSG顶部籽晶法
1.A new Nd-activated nonlinear crystal,Na3(La1-xNdx)9O3(BO3)8(Nd:NLBO)with x=3%,was grown by the top-seeded solution growth(TSSG) method.采用顶部籽晶法生长出掺杂浓度为3%的Nd:Na3La9O3(BO3)8(Nd:NLBO)晶体。
2.Using top-seeded solution growth(TSSG) method with H3BO3(4N),Li2CO3(4N) and Cs2CO3(4N) as reactants and the mol ratio of Li2CO3:Cs2CO3:H3BO3=1∶1∶11,large CLBO crystal with dimensions of 65 mm×22 mm×12 mm had been grown,and the growth conditions of the CLBO crystal were studied.以高纯硼酸、碳酸锂和碳酸铯为原料,摩尔比硼酸:碳酸锂:碳酸铯=11∶1∶1,采用顶部籽晶法,生长出尺寸为65 mm×22 mm×12 mm CsLiB6O10(CLBO)单晶,探讨了影响CLBO晶体生长的因素。
6)bottom seeded solution growth底部籽晶法
1.A novel crystal growth technique, the bottom seeded solution growth (BSSG), has been developed for crystal growth from high temperature solutions.为了从高温溶液中生长非一致熔融的单晶材料,发展了一种叫做“底部籽晶法”的新生长方法。
延伸阅读
铝合金的羽毛状晶铝合金的羽毛状晶feathey crystal of aluminium alloy IUheJ旧deyumooZhuangJ旧g铝合金的羽毛状晶(feathey Crystal of alu-minium anoy)铝合金铸锭中柱状晶的变种，形状类似羽毛的晶粒。是铸锭缺陷的一种。形状近似直线状花边的羽毛状晶亦称为“花边状组织”。羽毛状晶成群出现，每群中羽毛状晶之间近似平行。羽毛状晶是双晶，以(111)晶面为双晶面。铝一镁系合金中的羽毛状晶如图所示。’ 产生羽毛状晶的工艺因素主要是:(1)熔体处于高温平稳状态，有较好的定向结晶条件。(2)在铸造温度下熔体停留时间过长，熔体过热和高度净化，减少结晶前沿形成晶核的数量。(3)合金中加入某些容易产生羽毛状晶的微量元素，如硼和错。 超硬铝合金、工业纯铝和高镁铝合金形成羽毛状晶的几率较大，而高强锻造铝合金2A70(LD7)、防锈铝合金 3A21(LF21)和含镁低于5%的铝镁系合金，基本上不形成羽毛状晶。 铸锭中存在羽毛状晶对其性能影响较大。在塑性加工过程中易在羽毛状晶的双晶面处产生裂纹。制品中残留的未完全破碎的羽毛状晶区会扩大使用性能的各向异性。蘸: 铝一镁系合金铸锭中的羽毛状晶偏光只100 (格长清)