1)paramagnetism[英][,p?r?'m?gnitiz?m][美][,p?r?'m?gn?,t?zm?]顺磁性
1.PauLi-paramagnetism of Weak Interaction Fermi Gas in the Weak Magnetic Field;弱磁场中弱相互作用费米气体的泡利顺磁性
英文短句/例句
1.of or relating to a paramagnet.属于或关于顺磁性的。
2.Superparamagnetic Fe_2O_3 microparticles as gastrointestinal contrast agent in magnetic resonance imaging超顺磁性Fe_2O_3用作磁共振胃肠对比剂
3.It is sometimes difficult to draw the line separating ferromagnetic from paramagnetic substances.严格区别铁磁性与顺磁性物质有时是很困难的。
4.PauLi-paramagnetism of Weak Interaction Fermi Gas in the Weak Magnetic Field;弱磁场中弱相互作用费米气体的泡利顺磁性
5.At room temperature all the metals are paramagnetic.在室温时，所有的金属都是顺磁性的。
6.GIPAW Calculation of EPR G Tensor of Paramagnetic MoleculeGIPAW方法计算顺磁性分子EPR_g因子的研究
7.Preparation and characterization of super-paramagnetic MFe_2O_4 nanoparticles超顺磁性MFe_2O_4纳米粒子的制备及表征
8.Research on Origin Fitting Ni_2 FeAl SuperparamagneticOrigin法拟合Ni_2FeAl超顺磁性的研究
9.Transverse Relaxation Induced by Superparamagnetic Fe_3O_4 Nanoparticles超顺磁性纳米Fe_3O_4颗粒感生的横向弛豫
10.Synthesis and applications of superparamagnetic magnetite nanoparticles超顺磁性Fe_3O_4纳米颗粒的合成及应用
11.Experiment Research on Temperature Response of Faraday Effect in Paramagnetic Terbium Glass顺磁性铽玻璃法拉第效应温度特性实验研究
12.Synthesis, Characterization and Application of Mesoporous Superparamagnetic Nanoparticles;介孔超顺磁性纳米粒子的制备、性能及应用研究
13.The transition from ferromagnetism to paramagnetism involves a transition from ordered to disordered orientations of electron spins.由铁磁性转变为顺磁性涉及到电子自旋的取向由有序向无序转变。
14.Synthesis and Properties of Ultrasmall Superparamagnetic MRI Contrast Agent;超小型超顺磁性磁共振对比剂的制备及性能研究
15.Study of Super-paramagnetic Property of Silicon-oil-based Dysprosium Ferrite Magnetic Liquid硅油基镝复合铁氧体磁性液体的超顺磁性能研究
16.Development of α_vβ_3 integrin targeted superparamagnetic liposome and in vitro MR observationα_vβ_3整合素受体靶向性超顺磁性脂质体的建立及体外磁共振观察
17.Investigation of Superparamagnetic Nano-Spheres and Nano-Partical Synthesized Through Polyol Process多醇法制备超顺磁性Fe_3O_4纳米微球和颗粒的研究
18.Study on Transverse Relaxation of Water Protons Enhanced by Superparamagnetic Fe_3O_4 Particles超顺磁性Fe_3O_4颗粒增强水质子横向弛豫的研究
相关短句/例句
paramagnetic[英][,p?r?m?g'netik][美][,p?r?m?g'n?t?k]顺磁性
1.The magnetic suscepbility of MnFe Al_6 and MnFeSiAl_4 were measured by magnetic balance, it was proved that they were paramagnetic and could be separated by magnetic force.采用磁平衡法测量了MnFeAl_6和MnFeSiAl_42种金属间化合物的磁化率,证明它们是顺磁性的物质,利用磁场力可以将其分离。
3)superparamagnetic超顺磁性
1.Advancement of Research about Superparamagnetic Contrast Agents;超顺磁性造影剂的研究进展
2.Synthesis of superparamagnetic carboxyl functional magnetite microspheres through polyol process多醇法可控制备羧基化Fe_3O_4超顺磁性微球
3.Superparamagnetic Fe_2O_3 microparticles as gastrointestinal contrast agent in magnetic resonance imaging超顺磁性Fe_2O_3用作磁共振胃肠对比剂
4)superparamagnetism[,sju:p?,p?r?'m?ɡnitiz?m]超顺磁性
1.Preparation and superparamagnetism of Fe_3O_4 nanoparticles;Fe_3O_4纳米粒子的制备与超顺磁性
2.Preparation and Superparamagnetism of Nano-Ni/mesoporous SiO_2 Composites;纳米Ni/SiO_2介孔复合体的制备与超顺磁性
3.The results indicated that The introduction of MgO and Fe_3O_4 delays the transition from T-ZrO_2 to M-ZrO_2;the magnetic solid superacid catalysts have superparamagnetism because of the existence of Fe_3O_4 particles;The samples show well-defined crystallographic faces and the average size in diameter is 30nm;The HRTEM shows that .29nm;磁性基质的引入赋予了固体超强酸以超顺磁性;Hammett指示剂法测得经800℃焙烧后产物的酸强度Ho<-13。
5)super-paramagnetism超顺磁性
1.The results showed that the composite had super-paramagnetism, low water absorption and high tensile strength compared with pure PI.采用化学合成法及溶胶凝胶工艺制备了聚酰亚胺(PI)/纳米Fe2O3复合材料,采用古埃法、傅立叶变换红外光谱分析、吸水性能测试、拉伸性能测试等表征了材料的结构及特有的超顺磁性。
6)super paramagnetism超顺磁性
1.Results The synthesized Fe 3O 4 nanoparticles had super paramagnetism,its average diameter was 25nm.目的 采用水解法 ,在碱性条件下制备出具有超顺磁性的Fe3O4 纳米粒子。
2.The Cu/Fe quasi periodic super lattice sample with a Curie point higher than 300 K exhibits super paramagnetism at room temperature.进一步分析表明，超顺磁性的存在使得造成磁偶极分裂的磁场数值减小、超精细场减弱。
延伸阅读
顺磁性 一种弱磁性。从M＝кH的关系来看，磁化率к 是正的，即磁化强度M的方向与磁场强度H的相同,数量级在室温时一般为10-2～10-5emu。 从原子结构来看，组成顺磁性物体的原子、离子或分子具有未被电子填满的内壳层，也就是说具有原子、离子或分子磁矩。但是,这些磁矩之间没有相互作用,或者说，其相互作用与热运动能量相比是可以忽略的，因此，在热运动支配下，磁矩的取向是无规的。只有在外界磁场作用下，按照统计分布，沿磁场方向有一定的磁矩分量。在经典理论中,磁矩在磁场中可取任意方向,由统计力学所得到的磁化强度是， 式中 n 为单位体积的原子数，μ 为原子磁矩、L(α)＝称作朗之万函数，式中, t 为玻耳兹曼常数，T为绝对温度。若利用量子力学的结果,考虑到磁矩取向是量子化的，则磁化强度为 式中g为朗德因子，J为原子总角动量量子数，μB为玻尔磁子，称为布里渊函数， 在通常情况下，温度不很低、磁场不够强时，满足σ1的条件，朗之万函数或布里渊函数可在原点附近近似展开，而得到磁化强度的表达式为 这就是居里定律,它表明磁化率与温度成反比,其中是居里常数。由居里常数可测定原子的有效磁矩 一般的顺磁体遵从居里－外斯定律，即 式中C为居里常数，T为绝对温度，θ为一具有温度量纲的常数，反映了磁性原子之间尚有一定的相互作用。θ的符号可正可负，由相互作用的性质来决定。 典型的顺磁性气体是O2，常见的顺磁体有过渡族金属的盐类、稀土金属的盐类及氧化物。温度高于磁转变温度时，序磁性（见铁磁性）物质也呈现为顺磁性，如室温情况下除钆(Gd)以外的稀土金属。 在磁场作用下，正自旋和负自旋的传导电子具有不同的能量，这就导致在费密面附近有少量的传导电子自旋倒向，从而产生微弱的顺磁性效应。传导电子的顺磁性，也叫做泡利顺磁性，特点是与温度无关。 原子核具有磁矩时，在磁场作用下，也会产生顺磁性效应。但是原子核的顺磁磁化率约为10-10emu,在一般情况下，可忽略不计。