1)clean steel纯净钢
1.Production of Al-killed clean steel with 150 t ladle furnace;150t钢包炉生产铝镇静纯净钢的实践
2.Clean steel and technology of clean steel production;纯净钢及纯净铸坯的生产技术
英文短句/例句
1.Smelting Process and Its Results of Clean Steel Used for 1000 MW Nuclear Power Tube Plate1000MW核电管板用纯净钢的冶炼及效果
2.The test results showed that addition of La into the pure steel can modify the inclusion and improve the morphology of the inclusion thus to improve the corrosion resistance of the pure steel.试验结果表明,镧加入纯净钢中,可变质夹杂物和改善夹杂物形态,从而提高了纯净钢耐腐蚀性能。
3.Dirty steel due to entrapment of slag or pieces of refractory.因夹杂炉渣或耐火材料颗粒而造成的不纯净钢。
4.Manufacturing process and mechanical properties of forged clean steel tubesheets for 1000 MW nuclear power plant1000MW核电管板纯净钢锻件制造工艺及其性能
5.This paper describes that the work has been done in smelting process and production of clean steel in No.3 Steelmaking Plant of WISCO during recent years.介绍了近年来武钢第三炼钢厂在纯净钢冶炼工艺和生产方面所做的工作。
6.Analysis on the purity of molten steel for typical steel grades of No.3 Steelmaking Plant of Jinan Steel济钢三炼钢典型钢种钢水纯净度分析
7.Study of Microstructure of Ultrafined Ultrapure 42CrMoVNb Steel;超细化超纯净42CrMoVNb钢的微观组织研究
8.Fatigue Properties of Martensitic Stainless Steels with Ultra-low Carbon and High Cleanliness;纯净超低碳马氏体不锈钢材料的疲劳性能研究
9.Effect of Synthetic Slag During Converter Tapping on Cleanliness of 45 Steel转炉合成渣洗工艺对45钢纯净度的影响
10.Optimization of production process for 18-8 grade clean stainless steel and its effect18-8型纯净不锈钢生产工艺优化及其效果
11.Effect of RE on Cleanliness,Udercooling,Structure and Properties of Steel 4137H稀土对4137H钢纯净度、过冷度、组织及性能的影响
12.Selective material: select excellent imported stainless steel( SUS304-2 B), pure water, erosion resistant.选材精：选用优质进口不锈钢村（US304-2B）水质纯净，耐锈蚀。
13.Study on the Heat-treatment Parameters, Microstructures and Properties of ZDPH Highly Purified Forging Steels for Brake DiscsZDPH高纯净锻钢制动盘材料热处理工艺及组织性能研究
14.purifying apparatus提纯仪器;净化设备;净化设备;净化仪器;净化仪器
15.Being authentically or genuinely such by birth.纯种的出身纯正或血统纯净的
16.pure air and water; pure gold; pure primary colors; the violin's pure and lovely song; pure tones.纯净的空气和水；纯金；纯净的三原色；小提琴纯净可爱的歌唱；纯净的音色。
17.The key to reduce the wheel tyre quality problems is not only to optimize the wheel tyre design,but also to improve purity of steel.减少车轮轮箍质量问题的关键不仅要优化车轮轮箍设计 ,而且更要提高钢质纯净度。
18.perfect or complete or pure.完全、完整或者纯净。
相关短句/例句
pure steel纯净钢
1.The total amount of La of pure steel and the content of inclusion is determined with ion spectrum and low temperature electrolysis method,the amount of La in solid solution of pure steel is analyzed.采用离子光谱分析法和无水电解液低温电解法测定钢中的稀土La的总量和夹杂物含量,分析纯净钢中稀土La的固溶量,采用金相显微镜观察钢微观组织,研究固溶La对钢退火组织的影响。
2.25V pure steel and lucubrated the smelting process of the low-silicon steel , and put forward the process for pre-deoxidization by LF with Al and smelt by VD as well as the concept for strictly preventing molten steel from re-oxidation during vacuum pouring, meanwhile the double airproof protector for pouring box was fabricated.25V纯净钢的冶炼难点,同时对低硅钢的冶炼工艺进行了深入的分析研究,提出了采用钢包炉用铝预脱氧并进行VD的冶炼工艺方案和真空浇注过程中严密保护防止二次氧化的工艺思路,并制作了中间包双气封保护装置,实际使用效果十分理想,所炼钢的质量达到了纯净钢的要求。
3.Study is made of the impact of La on the corrosion resistance of pure steel through the observation of the morphology of RE inclusion in the pure steel,testing of electro-chemic corrosion EIS and polarization curve.通过观察纯净钢中稀土夹杂物的形态,测试电化学腐蚀EIS谱和极化曲线,研究稀土元素镧对纯净钢耐腐蚀性能的影响。
3)purity steel纯净钢
1.The effect of La on the high temperature oxidation of purity steel;La对纯净钢抗高温氧化性能的影响
2.Influence of La on microstructure of purity steel;稀土镧对纯净钢组织的影响
3.In this paper,the concepts of purity steel and clean steel are discussed The technology of controlling C,S,P,N,H,O in steel is summarized Some useful references of purity steel production can be drawn for domestic steel companie简要探讨了纯净钢和洁净钢的概念,概述了近20年来国内外主要钢厂生产纯净钢过程中控制钢中杂质元素(主要是C、S、P、N、H、O)的技术进展,为我国纯净钢生产提供了有益的借鉴。
4)high purity steel高纯净钢
1.Observation of microstructure during Cu precipitating in high purity steel;铜在高纯净钢中析出过程的观察
2.Alloying effect of La in high purity steel was investigated.通过对L a在高纯净钢中合金化作用的研究,结果表明,固溶L a对γ→α相变产生明显的影响,细化铁素体晶粒,提高了硬度。
5)Ultra-High Clean Steel超纯净钢
6)Super Clean IF steel高纯净IF钢
延伸阅读
45钢和40Cr钢调质的热处理工艺45钢40Cr钢调质调质是淬火加高温回火的双重热处理，其目的是使工件具有良好的综合机械性能。调质钢有碳素调质钢和合金调质钢二大类，不管是碳钢还是合金钢，其含碳量控制比较严格。如果含碳量过高，调质后工件的强度虽高，但韧性不够，如含碳量过低，韧性提高而强度不足。为使调质件得到好的综合性能，一般含碳量控制在0.30~0.50%。调质淬火时，要求工件整个截面淬透，使工件得到以细针状淬火马氏体为主的显微组织。通过高温回火，得到以均匀回火索氏体为主的显微组织。小型工厂不可能每炉搞金相分析，一般只作硬度测试，这就是说，淬火后的硬度必须达到该材料的淬火硬度，回火后硬度按图要求来检查。工件调质处理的操作，必须严格按工艺文件执行，我们只是对操作过程中如何实施工艺提些看法。1、45钢的调质45钢是中碳结构钢，冷热加工性能都不错，机械性能较好，且价格低、来源广，所以应用广泛。它的最大弱点是淬透性低，截面尺寸大和要求比较高的工件不宜采用。45钢淬火温度在A3+(30~50)℃，在实际操作中，一般是取上限的。偏高的淬火温度可以使工件加热速度加快，表面氧化减少，且能提高工效。为使工件的奥氏体均匀化，就需要足够的保温时间。如果实际装炉量大，就需适当延长保温时间。不然，可能会出现因加热不均匀造成硬度不足的现象。但保温时间过长，也会也出现晶粒粗大，氧化脱碳严重的弊病，影响淬火质量。我们认为，如装炉量大于工艺文件的规定，加热保温时间需延长1/5。因为45钢淬透性低，故应采用冷却速度大的10%盐水溶液。工件入水后，应该淬透，但不是冷透，如果工件在盐水中冷透，就有可能使工件开裂，这是因为当工件冷却到180℃左右时，奥氏体迅速转变为马氏体造成过大的组织应力所致。因此，当淬火工件快冷到该温度区域，就应采取缓冷的方法。由于出水温度难以掌握，须凭经验操作，当水中的工件抖动停止，即可出水空冷（如能油冷更好）。另外，工件入水宜动不宜静，应按照工件的几何形状，作规则运动。静止的冷却介质加上静止的工件，导致硬度不均匀，应力不均匀而使工件变形大，甚至开裂。