1)Mold Oscillation结晶器振动
1.The temperature at the meniscus during continuous casting was measured under mold oscillation by model experiments.设计了连铸结晶器弯月面处传热模拟实验,测量了在结晶器振动情况下弯月面处的温度,发现该处的温度随着结晶器的振动而产生周期性的变化。
2.The high temperature mechanical property of steel 20G is measured,the secondary cooling equipment is revamped and process parameters such as superheat,mold oscillation,secondary cooling water distribution are adjusted.为提高产能,对圆坯连铸机进行了提拉速工业试验,测定了试验钢种20G的高温力学性能,对二冷设备进行了改造,对钢水过热度、结晶器振动参数及二冷配水等工艺参数进行了调整。
3.In order to study the effect of mold oscillation on initial shell stress state,stress simulation model was set up by using the Marc software.为研究结晶器振动对初生坯壳应力状态的影响,利用Marc软件建立了结晶器内初生凝壳的应力计算模型,分析了振动过程中凝壳上应力和应变的分布规律。
英文短句/例句
1.Research and Development on Oscillation Monitoring and Analysis System of Continuous Casting Mould;结晶器振动状态监测分析系统的研制
2.Research on Control Model and Monitor System of Mould Oscillation;结晶器振动控制模型与监测系统研究
3.The Software Development of Mould Oscillation Detection and Analysis System;结晶器振动检测与分析系统软件开发
4.Application of Variable Parameters PID Controller for Model Oscillation of Caster变参数PID在铸机结晶器振动中的应用
5.Apply FM458 on Mould OscillationFM458在连铸机结晶器振动中的应用
6.Development of Online Vibration Monitoring System for a Mold Oscillation结晶器振动状态在线检测系统的研制
7.Development of mould oscillation machine of curved billet CCM弧形小方坯连铸机结晶器振动装置的发展
8.THE OPTIMIZATION OF OSCILLATION DATE OF No.1 CCM AT MEISHAN梅山1号连铸机结晶器振动参数的优化
9.Research Of Hand-held Detecting Equipment Based On the Mold Vibration Detection基于结晶器振动的手持式检测仪的研制与开发
10.Research and Development of Mould Vibration Detecting System Based on Embedded Technology手持式结晶器振动检测系统开发与应用
11.Mold Vibration Detection and Research Of Hand-held Detecting Equipment结晶器振动检测与手持式检测仪的研制
12.Design and application of a portable mould vibration monitoring system便携式结晶器振动监测系统的设计与应用
13.Study on Non-sinosoidal Oscillation System by Electrical Drive for Continuous Casting Mold连铸机结晶器电动式非正弦振动研究
14.Research of ccm mould no -sin vibration mode连铸机结晶器非正弦振动模式的研究
15.amplitude-modulated junction transistor oscillator调幅结形晶体管振荡器
16.Simulation & Control Strategy Research of the Hydraulic Vibration System for Crystallizer;结晶器液压振动系统仿真及其控制策略研究
17.Research of Control System for Continuous Casting Mould Oscillation Driven by Hydraulic Servo;连铸结晶器液压伺服振动控制系统研究
18.Design and Optimization of New Whole-Leaf Spring Oscillator for Mould;新型结晶器全板簧振动装置的设计与优化
相关短句/例句
Mould Oscillation结晶器振动
1.Influence of Mould Oscillation Parameters on Surface Quality of Concasting Billet;结晶器振动参数对连铸坯表面质量的影响
2.The Software Development of Mould Oscillation Detection and Analysis System;结晶器振动检测与分析系统软件开发
3.The influence of mould oscillation on surface quality of continuous cast slabs is introduced.论述了结晶器振动对连铸坯表面质量的影响 ,归纳出一些对生产实际和科研都有指导价值的结
3)mould hydraulic oscillation结晶器液压振动
1.In terms of equipment,measures taken include small pitch,split roll,continuously bending and straightening,soft reduction segments,mould hydraulic oscillation,mould electromagnetic brakes,fine control over mould level,longer vertical section of the caster,ladle slag detection,big concavity tundish and tundi.在设备方面采用了小辊密排、分节辊布置、连续弯曲和连续矫直,轻压下扇形段,结晶器液压振动,结晶器电磁制动,高精度的结晶器液面控制,较长的铸机垂直段,大包下渣检测,大容量中间包及对中间包吹氩;在工艺方面采用先进的一冷、二冷技术,动态轻压下;其他管理方面采用质量管理和对铸机进行定期检查维护等措施。
4)crystallizer vibro-bench结晶器振动台
5)vibrating mechanism of freezer结晶器振动机构
1.Present a method of dynamics analysis for vibrating mechanism of freezer of continuous casting machine.基于ADAMS软件,建立连铸机结晶器振动机构动力学仿真系统,得到高频振动条件下的动力学参数。
6)Mould Oscillating结晶器振动装置
1.Study of Remote Monitoring System for Slab Continuous Casting Mould Oscillating Based on ARM;基于ARM的板坯连铸机结晶器振动装置远程监测系统
延伸阅读
结晶器振动结晶器振动oscillation of mould 罐蒸瞧巍夔度慢，上升时间长，下降速度快，下降时间短。其效果是结晶器振动参数主要有:振幅S(mm)、振动频…朴焦…游扮、*、己~、、二、。二。、二、、拓二，r二，。‘，。，。。。f，2兀Z、二n n .1+a二确定之后，要选择结晶器振动的结构型式。(见结晶器vm上一2昭尸泛cos(兴冷t)t。[专专+号若](l)仰瓜~，曰’热~J十“目”口勺汀刀从叨目J户目，，~的“、2.“。“目帕“m上““以1+a‘。。、1+a，产‘￡‘ff’Zf:振动装置)任何振动机构都必须满足两个基本条件:。。f二2叮，1+a、二，，、*、。。，、，二、。，*二“、**、，_、法一。vm下-一2心尸吮cosL子=二(t一兰下今牙二)」(l)使结晶器准确地沿着一定的轨迹振动;(2)使结晶“m『“‘1一矿““‘1一。、’Zf’“器按要求的振动方式振动。才汇今+聆粤二(2) “礼f’Zf fJ 式中n一。，1，2，…，由式(1)，可得结晶器上升的最大 速度: 2兀Sj 月。二工vm=于升‘(3) I“。=了，一“1+口 }}由式(2)可得负滑时间及负滑时间率: !曰.叫1 60(1一a)尸(1一a)v。， !11}tN=二止公兰下二are eos[共万影拼〕(4) }厂、/叹z人l，，“”叮““‘“。‘27rs.f 昌}//)‘\少厂/z‘_，、，2(1一a)，(1一a)v。，___ 住}l///\礴了讣//尸3 NsR一~二二乙areeos仁月沈瑟手型]X100%(5) 招l了/洲/义弗盯//一’~二“‘”‘~‘2兀仅f 理11//从协/___.(_、__-一 蒋以/飞f结晶器的负滑量为: ”l低IINs一l一(v耐一vc)dt(6) }。=血x:。00/o、\\////式中v。为拉坯速度，m/min;才1、tZ分别为负滑开始和 }一“又少()咬了终了时间，s。负滑量的大小为图3中的阴影面积。它表 示在负滑动时间内结晶器相对坯壳的下移距离。负滑 图2结晶器振动位移曲线量越大对坯壳的压合效果越好。结晶器的振动一方面 促使润滑剂和保护渣填充到结晶器与坯壳间，形成润 滑层，以减小结晶器与坯壳的摩擦阻力，减少拉裂;另 一方面则在铸坯表面形成振痕，使结晶器与坯壳间的 。八/气隙增大，降低了坯壳凝固生长速度，造成坯壳凝固组 健}下{织中产生缺陷，影响了铸坯的表面质量。