1)transverse crack横裂纹
1.Analysis on transverse crack of Nb containing steel slab and improvement measures;含铌钢铸坯横裂纹的分析及改进措施
2.An Analysis on Forming Cause of Surface Transverse Crack of 1900 mm Continuous Casting Slab;1900mm连铸板坯表面横裂纹成因的分析
3.The influence factors of transverse crack formation have been discussed,and then the effective measures have been proposed to reduce the transverse crack.通过对邯钢三炼钢厂板坯连铸生产高强度船板用等铌微合金钢,铸坯发生表面横裂纹的机理分析,讨论了铸坯表面横裂纹产生的影响因素,并提出了连铸解决含铌钢表面横裂纹的有效措施。
英文短句/例句
1.Transverse crack analysis of SWRH 82B wire rod drawingSWRH82B盘条拉拔横裂纹分析
2.Analysis and Control Measures on Transversal Crack of Nb Containing Slab含铌钢铸坯横裂纹的分析及控制措施
3.Analysis and Controlling Methods on Transverse Cracks of Plate Nb Containing Steel Slab中厚板含铌钢铸坯横裂纹分析及控制措施
4.Study on Transversal Corner Crack of 15Mn2CrVNb Bloom for Wagon Brake Beam Manufacturing货运机车制动梁用15Mn2CrVNb钢方坯角部横裂纹研究
5.STUDY ON TRANSVERSE CORNER CRACKING OCCURRENCE PREVENTION?OF THE Nb,V AND Ti MICROALLOYING STEEL CC SLABS减少含铌、钒、钛微合金化钢连铸板坯角横裂纹的研究
6.The Causes of Formation and Measures of Control about Corner Transverse Cracks on Slab with Nb Alloy in Ansteel 2150 mm ASP Product Line鞍钢2150mm ASP生产含铌合金钢铸坯角部横裂纹的成因及控制
7.Floor-beam webs have cracked in tied arch bridges.在系干拱桥的横梁腹板上发生裂纹。
8.Analyses of cause for transverse cracks on CC slab surface连铸板坯表面横向裂纹产生原因分析
9.Analysis of Fundamental Frequencies of Rotating Shafts with Transverse Crack;含横向裂纹的转动轴的振动基频分析
10.Judge of Transverse Crack of Thick-Walled Seam by Ultrasonic Testing Method厚壁焊缝横向裂纹的超声波判别方法
11.Numerical Analysis of Transversal Crack on Slab Corner in Straightening During Continuous Casting连铸矫直过程板坯角部横向裂纹数值分析
12.Analysis and Improvement of Side Beam Crack in Joint Wagon关节车端横梁裂纹原因分析及改进方案
13.Dynamic analysis of rotor system with transverse crack based on finite element基于有限元的横向裂纹转子系统的动力学分析
14.Three-dimensional numerical analysis of cracks in transversely isotropic materials横观各向同性材料三维裂纹问题的数值分析
15.Influence of transverse crack model on shafting's torsional shear stress轴系横向裂纹模型对其扭转剪应力的影响
16.Mechanical Cause and Safe Crack Scale Estimation of Transverse Crack on Tube Inner Surface身管内表面横纹萌生的力学成因及安全裂纹尺度估计
17.a broken back is nothing to be casual about; it is no fooling matter.横向的裂纹不是什么可以随便处之的事情；不是玩笑。
18.Often lack of fusion adjacent to the girder web in the transverse groove welds led to the cracking.在靠近主梁腹板的横向坡口焊缝处常常出现未熔透而导致裂纹。
相关短句/例句
Transverse cracking横裂纹
1.Slab surface transverse cracking has found to occur at bending or straightening of continuous casting strand, and is related with hot ductility around Υ-α transformation temperature.在钢坯表面上的慢冷使横裂纹在实验上再现,即传统冷却方式可以产生具有片层状铁素体的正常微观结构。
3)horizontal crack横裂纹
1.To analyze the cause for horizontal crack on the surface of 30MnSi continuous casting billet.对30MnS i连铸方坯表面横裂纹产生的原因进行了分析。
4)cross crack横裂纹
1.Comprehensively analyzed the reasons of cross crack caused by HRB335 steel and results by taking corresponding measures.主要对 HRB335钢产生横裂纹的原因进行全面的分析 ,以及采取相应的措施取得的效果。
5)Transversal Crack横裂纹
1.A new method,by which the formation process of surface transversal crack on slab is simulated with notched specimen,is proposed in this paperThe importance of investigating hightemperature fracture mechanical property of the metal for defect avoidance on slabs is also indicated,and some experimental results are introduce通过一种新的试验研究方法，即利用含缺口试样模拟铸坯表面横裂纹的产生过程，指出了材料高温断裂力学性能在研究连铸坯缺陷中的重要意义，并介绍了部分试验研究结果。
6)transverse crack横向裂纹
1.Influence of Strength Matchings on the J-Integral ofWelded Joints With Transverse Cracks;强度组配对含有横向裂纹焊接接头J积分的影响
2.Study on causes of transverse cracks in main beam of PC cable-stayed bridge from forces analysis;从受力角度谈PC斜拉桥主梁横向裂纹产生原因
3.Cause analysis on transverse cracks of water-cooling wall tubes in Ningxia Dawukou Power Plant;国电宁夏大武口发电厂水冷壁管横向裂纹原因分析
延伸阅读
淬火裂纹和非淬火裂纹的特征及实例分析淬火裂纹是指在淬火过程中或在淬火后的室温放置过程中产生的裂纹。后者又叫时效裂纹。造成淬火开裂的原因很多，在分析淬火裂纹时，应根据裂纹特征加以区分。 一、淬火裂纹的特征 在淬火过程中，当淬火产生的巨大应力大于材料本身的强度时，便会导致裂纹产生。淬火裂纹往往是在马氏体转变开始进行后不久产生的，裂纹的分布则没有一定的规律，但一般容易在工件的棱角槽口、截面突变处形成。 在显微镜下观察到的淬火开裂，可能是沿晶开裂，也可能是穿晶开裂；有的呈放射状，也有的呈单独线条状或呈网状。 因在马氏体转变区的冷却过快而引起的淬火裂纹，往往是穿晶分布，而且裂纹较直，周围没有分枝的小裂纹。 因淬火加热温度过高而引起的淬火裂纹，都是沿晶分布，裂纹尾端尖细，并呈现过热特征：结构钢中可观察到粗针状马氏体；工具钢中可观察到共晶或角状碳化物。 表面脱碳的高碳钢工件，淬火后容易形成网状裂纹。这是因为，表面脱碳层在淬火冷却时的体积胀大比未脱碳的心部小，表面材料受心部膨胀的作用而被拉裂呈网状。 二、非淬火裂纹的特征 淬火后发生的裂纹，不一定都是淬火所造成的，一般可根据下面的特征来区分。 淬火后发现的裂纹，如果裂纹两侧有氧化脱碳现象，则可以肯定裂纹在淬火之前就已经存在。淬火冷却过程中，只有当马氏体转变量达到一定数量时，裂纹才有可能形成。与此相对应的温度，大约在250℃以下。在这样的低温下，即使产生了裂纹，裂纹两侧也不会发生脱碳和出现明显氧化。所以，有氧化脱碳现象的裂纹是非淬火裂纹。 如果裂纹在淬火前已经存在，又不与表面相通，这样的内部裂纹虽不会产生氧化脱碳，但裂纹的线条显得柔软，尾端圆秃，也容易与淬火裂纹的线条刚健有力，尾端尖细的特征区别开来。 三、实例分析 实例一： 40Cr钢制成的转子轴，经锻造、淬火后发现裂纹。裂纹两侧有氧化迹象，经金相检验，裂纹两侧存在脱碳层，而且裂纹两侧的铁素体呈较大的柱状晶粒，其晶界与裂纹大致垂直。结论：裂纹是在锻造时形成的非淬火裂纹。 当工件在锻造过程中形成裂纹时，淬火加热即引起裂纹两侧氧化脱碳。随着脱碳过程的进行，裂纹两侧的碳含量降低，铁索体晶粒开始生核。当沿裂纹两侧生核的铁素体晶粒长大到彼此接触后，便向离裂纹两侧较远的基体方向生长。由于裂纹两侧在脱碳过程中碳浓度的下降，也是由裂纹的开口部位向内部发展，因而为铁素体晶粒的不断长大提供了条件，故最终长大为晶界与裂纹相垂直的柱状晶体。