bismuth tellurideBi2Te3
1.Novel rare-earth contained bismuth telluride thermoelectric materials were prepared by solvothermal synthesis at 180℃ using bismuth chloride, tellurium powder and lanthanum chloride or oxide as starting materials, and the following hot uniaxial pressing (HUP), 400℃, at 50()MPa for 1h.以氯化铋、碲粉、氯化镧或氧化镧为原料,采用180℃溶剂热合成和400℃、50MPa、1h热压技术制备了含稀土的新型Bi2Te3基热电材料。
2.Bismuth telluride P type semiconductor refrigerating material was fabricated by Solid-State Reaction and Agglomeration using Bi and Te.以Bi和Te的单质为原料,用固相反应烧结法制备Bi2Te3P型半导体制冷材料。
3)Bi 2Te 3-Sb 2Te 3-Sb 2Se 3Bi2Te3-Sb2Te3-Sb2Se3
1.The powders of N-type and P-type pseudo-ternary(Bi 2Te 3-Sb 2Te 3-Sb 2Se 3)thermoelectric materials were prepared by mechanical alloying method.本文采用机械合金化法成功制备了N型和P型赝三元(Bi2Te3-Sb2Te3-Sb2Se3)合金粉体材料,利用XRD和SEM对材料的合金化程度和材料粉体粒度进行了分析,该材料颗粒均匀、细小,颗粒尺寸平均在100nm量级左右。
4)Bi_2Te_3 based alloysBi2Te3基合金
5)Bi2Te3Bi2Te3化合物
1.The results showed that the Bi2Te3 powder of nanostructure was flower-like clusters.采用溶剂热法制备纳米结构的Bi2Te3化合物,以氯化铋,亚碲酸钠,氢氧化钠,表面活性剂EDTA二钠,以及还原剂硼氢化钠为初始原料,将初始原料的混合水溶液加入到聚四氟乙烯为内衬的不锈钢反应釜容器内,经过超声波振动30min后,在423～473K热处理24～72h后得到黑色粉末产物,用去离子水和无水乙醇反复洗涤除去产物中的可溶性离子和有机物,并在333K下真空干燥,最后得到花簇状的Bi2Te3化合物粉体,并对产生花簇状的原因进行了分析和阐述。
6)p-type Bi2Te3p型Bi2Te3