1)Nanosheets纳米薄片
1.TiO_2 nanosheets were prepared through hydrothermal chemical process.研究了水热化学处理法制备TiO2纳米薄片的条件,以光催化降解苯酚为模型反应,考察了TiO2纳米薄片及其焙烧产物的光催化反应性能。
2.Photocatalytic Degradation of Anthraquinone Dye B-RN by NiO Nanosheets;采用水热法制备NiO纳米薄片,用XRD和TEM对样品的晶型及颗粒形貌进行了表征。
英文短句/例句
1.Graphite Oxide Nanoplatelets Surface Graft Polyethylene Glycol氧化石墨纳米薄片表面接枝聚乙二醇(英文)
2.Preparation of Mixed Mg-Al Oxide Nanoflakes with a High Specific Surface Area and Its Enhanced Adsorptive Power高比表面积的镁铝复合氧化物纳米薄片的制备及其吸附性能
3.Preparation of Nano-(Micro-) Crystal Thin Films on Self-Source Substrate;反应性基片上制备纳米（微米）晶薄膜
4.Hydrothermal Synthesis of the Mn_xZn_(1-x)O Crystal and the Crystal Sheet of Nano Boehmite;水热法合成Mn_xZn_（1-x）O晶体和纳米薄水铝石晶片
5.Fabrication and Property Studies of Titania Nanosheets Composite Film;氧化钛纳米片复合薄膜的制备及其性能研究
6.Aluminum Pigments Encapsulated with Nano-SiO_2 Coatings and Their Acid-resistance纳米SiO_2包覆改性薄片铝粉颜料及其耐酸性研究
7.Study of Nonlinear Conduction Behavior of Silicone Rubber/Graphite Nanosheet Composites under Pressure Field;硅橡胶/纳米石墨薄片复合材料在压力场作用下电导非线性研究
8.The Study of Nonlinear Conduction of Polyethylene/graphite Nanosheet Nanocomposite under External Fields;聚乙烯/纳米石墨薄片复合材料在外场作用下电导非线性的研究
9.Dispersion of Graphite Nanosheets in Polymer Resin Via Masterbatch Blending and the Structure and Properties of the Nanocomposites;纳米石墨薄片的母料法分散及其复合导电材料的结构与性能
10.Growing ZnO Nanoparticles on Si Substrates by Implantation and the Effect to Growth Behavior of ZnO Film离子注入Si基片生长ZnO纳米团簇及其对ZnO薄膜生长行为的影响
11.Effect of borneol/mentholum eutectic mixture on nasal-brain delivery of neurotoxin loaded nanoparticles冰片-薄荷脑低共熔物对神经毒素纳米粒鼻腔给药载药入脑的影响
12.The research of nanoGs/PANI-PEG-PANI composites and conductivity纳米石墨薄片/聚苯胺-g-聚乙二醇复合材料及导电性能
13.thin piece of cornmeal dough fried.油炸的、薄的玉米粉面片。
14.Preparation of Au Nanometer Thin Film Using Silicon Nanoporous Array as Template以硅纳米孔柱阵列为模板制备金纳米薄膜
15.Every its bunch ferrite consists of many phase-equal ferrite thin slices with thickness of about 200nm.其征一束针状铁素体由许多位相相同，厚度大约200纳米的薄铁素体片组成。
16.Selective Synthesis of FeS and FeS_2 Nanosheet Films on Iron Substrate for Double-photoelectrode Dye-sensitized Solar Cells;铁基底上选择性合成FeS和FeS_2纳米片薄膜及其在双光电极太阳能电池中的应用
17.The Research of Hydrogenated Nanocrystalline-Amorphous Silicon Thin-Film Solar Cells;氢化纳米硅（na-Si：H）薄膜太阳电池研究
18.Solid State Reaction Mechanism in Interfaces of Fe/Ti Nanometer-Scale Multilayers;Fe/Ti纳米多层薄膜界面反应机制研究
相关短句/例句
Nanosheet纳米薄片
3)graphite nanosheets纳米石墨薄片
1.Synthesis and characterization of polyaniline/graphite nanosheets/Eu~(3+) nanocomposites through emulsion polymerization;乳液聚合法制备聚苯胺/纳米石墨薄片/Eu~(3+)纳米复合材料及其导电性能
2.Dispersion of Graphite Nanosheets in Polymer Resin Via Masterbatch Blending and the Structure and Properties of the Nanocomposites;纳米石墨薄片的母料法分散及其复合导电材料的结构与性能
3.The structural relation about graphite, expandable graphite, expanded graphite, graphite nanosheets, graphite/ bismaleimide composites and graphite nanosheets/bismaleimide composites was studied by XRD spectrum, and the effect of BMI monomer on graphite intercalating space in graphite/ bismaleimide composites and graphite nanosheets/bismaleimide composites was also studied.利用X射线衍射对鳞片石墨、可膨胀石墨、膨胀石墨和纳米石墨薄片以及石墨 /双马来酰亚胺、纳米石墨薄片 /双马来酰亚胺减摩复合材料进行了研究,探讨它们之间在结构上的关系以及以复合材料中双马来酰亚胺预聚体对石墨层间距的影响。
4)titanate nano-thickness sheets钛酸纳米薄片
5)Fe 65 Co 18 Ni 7 Si 1 B 9 nanoflakesFe65Co18Ni7Si1B9薄片状纳米晶微粉
6)nano-films纳米薄膜
1.Properties of Co nano-films deposited on monocrystalline silicon surface by ion beam sputtering;单晶Si表面离子束溅射沉积Co纳米薄膜的研究
2.Study on surface morphology and microstructure of Al_2O_3 nano-films prepared by ion beam sputtering deposition离子束沉积Al_2O_3纳米薄膜微观结构及形貌研究
3.The characterization of thermoelectric properties of semiconductor nano-films on methods and relative theories are reviewed.综述了半导体纳米薄膜热电性能表征的方法及相关的技术原理。
延伸阅读
看纺织印染中应用纳米材料和纳米技术纺织印染中应用纳米材料和纳米技术时，除了要解决纳米材料的制备技术之外，重要的是要解决好纳米材料的应用技术，其中关键问题是使纳米粒子和纺织印染材料的基本成分（即聚合物材料）之间处于适当的结合状态。印染中，纳米粒子在聚合物基体中的分散和纳米粒子在聚合物表面的结合是主要的应用技术问题。 制备聚合物/无机纳米复合材料的直接分散法，适用于各种形态的纳米粒子。印染中纳米粒子的使用一般采用直接分散法。但是由于纳米粒子存在很大的界面自由能，粒子极易自发团聚，利用常规的共混方法不能消除无机纳米粒子与聚合物基体之间的高界面能差。因此，要将无机纳米粒子直接分散于有机基质中制备聚合物纳米复合材料，必须通过必要的化学预分散和物理机械分散打开纳米粒子团聚体，将其均匀分散到聚合物基体材料中并与基体材料有良好的亲和性。直接分散法可通过以下途径完成分散和复合过程： 高分子溶液（或乳液）共混：首先将聚合物基体溶解于适当的溶剂中制成溶液（或乳液），然后加入无机纳米粒子，利用超声波分散或其他方法将纳米粒子均匀分散在溶液（或乳液）中。有人将环氧树脂溶于丙酮后加入经偶联剂处理过的纳米TiO2，搅拌均匀，再加入 40wt%的聚酰胺后固化制得了环氧树脂/TiO2纳米复合材料。还有人将纳米SiO2粒子用硅烷偶联剂处理后，改性不饱和聚酯。 熔融共混：将纳米无机粒子与聚合物基体在密炼机、双螺杆等混炼机械上熔融共混。如将PMMA和纳米SiO2粒子熔融共混后，双螺杆造粒制得纳米复合材料。又如利用偶联剂超声作用下处理纳米载银无机抗菌剂粒子，分散制得PP/抗菌剂、PET/抗菌剂、PA/抗菌剂等复合树脂，然后经熔融纺丝工艺加工成抗菌纤维。研究表明，将经过表面处理的纳米抗菌剂粒子通过双螺杆挤出机熔融混炼，在聚合物中可以达到纳米尺度分散，获得了具有良好综合性能的纳米抗菌纤维，对大肠杆菌、金黄色葡萄球菌的抗菌率达到95%以上（美国AATCC－100标准）。 机械共混：将偶联剂稀释后与碳纳米管混合，再与超高分子量聚乙烯（UHMWPE）混合放入三头研磨机中研磨两小时以上。将研磨混合物放入模具，热压，制得功能型纳米复合材料。 聚合法：利用纳米SiO2粒子填充（Poly（HEMA））制备了纳米复合材料。纳米SiO2粒子首先被羟乙基甲基丙烯酸（HEMA）功能化，然后与HEMA单体在悬浮体系中聚合。还有利用SiO2胶体表面带酸性，加入碱性单体4－乙烯基吡咯进行自由基聚合制得包覆型纳米复合材料。