等温淬火,austempering英语短句,例句大全

等温淬火,austempering
1)austempering[,?:s'temp?ri?]等温淬火
1.Effects of Si and Austempering on the Wearresistance Property of ZG30SiMnCr;Si及等温淬火工艺对ZG30SiMnCr耐磨性的影响
2.Effect of Austempering on Mechanical Properties and Abrasion-Resistance of Mn -Cr Alloyed White Cast Iron;等温淬火对Mn-Cr白口铸铁力学性能和耐磨性的影响
3.Research of austempering process of low-carbon ductile iron;低碳球铁的等温淬火工艺研究

英文短句/例句

1.austemper stressing等温淬火表面应力;等温淬火前加应力;加工应力等温淬火
2.Effect of Austempering on Mechanical Properties of Dual Phase ADI等温淬火工艺对双相等温淬火球墨铸铁力学性能的影响
3.Study on the Bainite Morphology of ADI等温淬火球铁贝氏体组织形态的研究
4.Study on the Wear Resistancl of ADI等温淬火奥—贝球铁抗磨性能的研究
5.Research on the Dummy Bar of Austempered Ductile Iron;等温淬火球铁(ADI)引锭杆的研制
6.Process Research on the Isothermal Quenching of Ductile Iron of Austenite and Bainite;奥氏体贝氏体球铁等温淬火工艺研究
7.Technical of Study Compound of 18Cr2Ni4WA Steel18Cr2Ni4WA钢复合等温淬火工艺研究
8.Austempering process of Cr12MoV steel thread rolling dieCr12MoV钢滚丝模等温淬火工艺
9.modified austemper(获得珠光体加贝氏体混合组织的)准等温淬火(如铅淬火)
10.On Quasi austempering Bainitic/Martensitic Ductile Iron Grinding Ball贝氏体/马氏体球铁磨球准等温淬火工艺的研究
11.The Investigation on Novel Heat Treatment Processes of Austempered Ductile Iron (ADI);等温淬火球墨铸铁（ADI）的新型热处理研究
12.Present Situation and Developing Prospect of Isothermally quenched Ductile Irons Production in China;我国等温淬火球铁的生产现状及发展前景
13.Study of Micro-alloying and Isothermal Quench of Steel Shots With High Toughness高韧性钢丸的微合金化及等温淬火工艺研究
14.Effect of Austerpering After Carburizing on Microstructure and Property of 18Cr2Ni4WA18Cr2Ni4WA渗碳后等温淬火对组织与性能的影响
15.Effect of Austempering Heat Treatment on Erosive Wear of Austenite Ductile Iron等温淬火处理对奥贝球铁冲刷磨损性能的影响
16.Study on Austempering Process Parameters of Modified Low Chromium White Cast Iron低铬变质白口铸铁等温淬火工艺参数的研究
17.Study on Microstructures and Mechanical Properties of Low-Alloyed High-Carbon Steels by Low-Temperature Isothermal Treatment;低合金高碳钢低温等温淬火组织和力学性能的研究
18.The microstructure of isothermally-quenched ductile iron (ADI) is a mixture structure consisting of austenite plus acicular ferrite.等温淬火球铁的显微组织由奥氏体加针状铁素体的混合组织组成。

相关短句/例句

isothermal quenching等温淬火
1.The results show that the better match of strength and toughness of 20Mn2SiVB steel can be obtained by isothermal quenching at 420℃.研究了20Mn2SiVB贝氏体钢经940℃完全奥氏体化后,再进行不同温度和时间的盐浴等温淬火,通过调整贝氏体的相对含量来控制材料热处理后的组织和综合力学性能。
2.Isothermal quenching treatment is one of effective methods to improve properties of austenitic-bainitic steel.等温淬火是提高奥氏体-贝氏体钢性能的重要手段,选择合理的奥氏体化温度对提高奥氏体-贝氏体钢性能具有重要意义。
3.The isothermal quenching process of the ductile iron camshaft was analyzed.对球铁凸轮轴的等温淬火工艺进行了分析,认为产生淬火裂纹的主要原因是:加热炉内的温度过高及等温槽内盐浴老化、等温淬火温度偏低。
3)isothermal hardening等温淬火
1.Strengthening and Toughening of Die Steel Cr7Mo3V2Si by Isothermal Hardening with Prenitriding and Diffusion;模具钢Cr7Mo3V2Si渗扩氮等温淬火复合强韧化
2.The influences of various isothermal hardening treatments on microstructure and properties of semi-steel made by quenching and isothermal hardening and forging,which contain 1.研究了空淬、等温淬火及锻热等温淬火对含1。
3.2)=900～1000 MPa,σ_b=1300～1564 MPa)and excellence plasticity(δ_5=15%～18%)were obtained after aus- tenitization at 840～880℃followed by isothermal hardening for 3 hours.试验用钢经840～880℃加热,保温20min,在320～360℃的盐浴炉中等温淬火3 h,得到较高的强度(σ_(0。
4)austempering treatment等温淬火
1.The influence of austempering treatment on the microstructure, retained austenite and fracture toughness of high silicon cast steel has been studied.研究了在不同等温淬火温度热处理后高硅铸钢的显微组织与残余奥氏体量和材料断裂韧性间的关系。
2.The results show that a pure ausferrite structure that consists of bainitic ferrite and carbon riched retained austenite can be obtained by austempering treatment of high silicon cast steel over a large temperature range (240～400℃).结果表明 ,高硅铸钢经等温淬火热处理后 ,在较大的温度范围 (2 4 0～ 4 0 0℃ )内都可以得到单一的由贝氏体铁素体和富碳的残余奥氏体交替排列的奥贝双相组织 (Ausferrite) ,组织中没有碳化物析出。
5)austemper[?:s'temp?]等温淬火
1.The compare of mechanical performance after austemper and oil quenching in high strength elasticity part of T8A metal strip was done.对T8A钢带用作高强度弹性零件时等温淬火与油冷淬火后的力学性能进行了比较,探讨了等温淬火的工艺参数对材料综合力学性能的影响,尤其对材料屈服强度的影响;针对具体零件,应用等温淬火工艺代替油冷淬火工艺,提高了零件的屈服强度,使零件在使用过程中的稳定性得到提高。
2.Bainite ductile cast iror is obtained by austempering at higher temperature.研究发现：在较高的温度下对球墨铸铁进行等温淬火处理得到的贝氏体球铁。
3.In this paper,under the conditions of austenitized at tempe- ratures ranging from 850℃ to 950℃ and austempered at temperatures ranging from 260℃ to 420℃,the austempering treatment of ductile iron was conducted.本文在850—950℃奥氏体化温度范围和260—420℃等温温度范围的条件下,对球墨铸铁进行等温淬火处理,制备了一组具有不同相对含量、不同形态和分布的奥氏体—贝氏体组织的试样。
6)Isothermal quench (1Q)等温淬火(IQ)