纳米MgO,nano-MgO
1)nano-MgO纳米MgO
1.Effect of Nano-MgO Particles on the Densification Properties and Conductivity of Nano- ZrO_2(3Y);掺纳米MgO第二相对ZrO_2(3Y)材料性能的影响
2.The results show that the diameter of nano-MgO particles are about 12 nm.以Na2CO3与MgCl2为原料,采用共沉淀法,在反应温度30℃,反应体系pH值10,550℃煅烧碱式碳酸镁条件下,制备纳米MgO,制得的纳米MgO平均粒径约12 nm。
英文短句/例句

1.Surface Modification of Nano-MgO with Titante Coupling Agent钛酸酯偶联剂改性纳米MgO的研究
2.SYNTHESIS OF BIOMORPHIC NANO-MAGNESIA USING COTTON FABRIC AS A TEMPLETE采用布模板合成生物形态纳米MgO
3.A Study on Nanocrystalline MgO Powders Prepared by a Gel-Combustion Synthesis Technology;凝胶—燃烧合成法制备纳米MgO颗粒的研究
4.Study of the Space Charge Behaviour in Polyethylene Doped with Nano-MgO纳米MgO掺杂聚乙烯中空间电荷行为的研究
5.Preparation of nanometer MgO and its application in antistatic finishing纳米MgO的制备及其在抗静电整理中的应用
6.SYNTHESIS OF MgO NANOCRYSTALLINE POWDER BY LOW-TEMPERATURE COMBUSTION低温燃烧法合成纳米MgO粉体工艺的研究
7.Study on Preparation, Surface-modification and Antibacterial Application in Interior-wall Paint of Nanometer MgO Powder;纳米MgO粉体的制备与改性及其在内墙涂料上的抗菌应用研究
8.Synthesis of N-doped and Undoped Carbon Nanotubes on Fe/MgO CatalystsFe/MgO催化合成碳纳米管和氮掺杂碳纳米管(英文)
9.Prepartion of Nano-Mg(OH)_2 and Nano-MgO Studay of Nano-Mg(OH)_2 and Nano-MgO;纳米Mg(OH)_2与MgO的制备及研究
10.Synthesis of nano-sized WC/MgO powders by reactive high-energy ball milling反应高能球磨制备纳米WC/MgO复合粉末
11.Preparation and Property of Ni-P-MgO(CuO) Electroless Namometer(Micron) Composite Coatings;Ni-P-MgO(CuO)纳米、微米复合化学镀层的制备和性质
12.Synthesis of Single-walled Carbon Nanotubes using alcohol as carbon source Mo-Co/MgO as catalysts乙醇做碳源Mo-Co/MgO做催化剂合成单壁碳纳米管
13.Preparation of MgO Nanoparticles by Ion Exchange Resin Homogenous Precipitation Method离子交换树脂均匀沉淀法制备MgO纳米粒子(英文)
14.Reaction mode and criterion of nanocomposite WC-MgO powders prepared by high-energy ball milling高能球磨制备纳米WC-MgO粉末的反应模式及判据
15.Study on Influencing Factors in Carbon Dioxide Reforming of Methane Over Nano-Ni/MgO Catalyst纳米Ni/MgO催化剂在CO_2重整CH_4反应中影响因素的研究
16.Synthesis of high purity multi-walled carbon nanotubes over Co-Mo/MgO catalyst by the catalytic chemical vapor deposition of methaneCo-Mo/MgO催化剂上甲烷化学气相沉积制备高纯度多壁碳纳米管(英文)
17.Promoting Effects of Chromium on Ni/MgO Catalysts for CNTs Synthesis by Chemical Vapor Deposition Method助剂铬对Ni/MgO催化剂CVD法制备碳纳米管的促进作用
18.Crystal-lattice Vibration and Electron-phonon Coupling Properties of Quasi-1-dimensional Short Wave-length ZnO/MgO Optoelectronic Nano-materials短波长纳米ZnO/MgO准一维光电材料的晶格振动及电子-声子相互作用耦合特性
相关短句/例句

Nanometer MgO纳米MgO
1.Preparation of Nanometer MgO and Stability of Red Phosphorus;纳米MgO的制备及对赤磷安定性研究
2.Preparation of nanometer MgO and its application in antistatic finishing纳米MgO的制备及其在抗静电整理中的应用
3.This paper discussed preparation of nanometer MgO with sedimentation method.所作主要工作如下:1)利用MgCl_2与Na_2CO_3为原料,采用共沉淀法,控制反应溶液的PH值、反应物浓度、反应温度,选择适当的反应时间和煅烧温度制备出纳米MgO粉体,通过透射电镜(TEM)、X射线衍射(XRD)、热重分析(TG)对样品的性能进行测试。
3)magnesium oxide nanocrystalliteMgO纳米晶
4)nanometer MgO/SiO_2纳米MgO/SiO_2
1.In order to study wear automatic restoration action of nanometer MgO/SiO_2 and the influence of frictional condition on automatic restoration,repairing action of nanometer MgO/SiO_2 to worn steel surface as an ad- dtive in 350SN oil is evaluated by using HQ-1 wear machine,and the influence of load,slide velocity and time on its au- tomatic restoration capability is also studied.为研究MgO/SiO_2复合纳米的磨损自修复作用及摩擦条件对修复的影响,将MgO/SiO_2复合纳米作为添加剂加入350SN基础油中,在HQ-1环块摩擦磨损试验机上考察了MgO/SiO_2复合纳米对磨损表面的修复作用,在不同的载荷、转速、修复时间条件下进行了修复试验,并探讨了摩擦条件对纳米MgO/SiO_2自修复性能的影响机理。
5)nano-MgO thin film纳米MgO膜层
1.Anti-corrosion nano-MgO thin films on sintered NdFeB magnet surface prepared by sol-gel method;Sol-gel法在烧结型NdFeB永磁材料表面制备耐蚀纳米MgO膜层的研究
6)nanocrystalline MgO powders纳米MgO颗粒
延伸阅读

看纺织印染中应用纳米材料和纳米技术纺织印染中应用纳米材料和纳米技术时,除了要解决纳米材料的制备技术之外,重要的是要解决好纳米材料的应用技术,其中关键问题是使纳米粒子和纺织印染材料的基本成分(即聚合物材料)之间处于适当的结合状态。印染中,纳米粒子在聚合物基体中的分散和纳米粒子在聚合物表面的结合是主要的应用技术问题。   制备聚合物/无机纳米复合材料的直接分散法,适用于各种形态的纳米粒子。印染中纳米粒子的使用一般采用直接分散法。但是由于纳米粒子存在很大的界面自由能,粒子极易自发团聚,利用常规的共混方法不能消除无机纳米粒子与聚合物基体之间的高界面能差。因此,要将无机纳米粒子直接分散于有机基质中制备聚合物纳米复合材料,必须通过必要的化学预分散和物理机械分散打开纳米粒子团聚体,将其均匀分散到聚合物基体材料中并与基体材料有良好的亲和性。直接分散法可通过以下途径完成分散和复合过程:   高分子溶液(或乳液)共混:首先将聚合物基体溶解于适当的溶剂中制成溶液(或乳液),然后加入无机纳米粒子,利用超声波分散或其他方法将纳米粒子均匀分散在溶液(或乳液)中。有人将环氧树脂溶于丙酮后加入经偶联剂处理过的纳米TiO2,搅拌均匀,再加入 40wt%的聚酰胺后固化制得了环氧树脂/TiO2纳米复合材料。还有人将纳米SiO2粒子用硅烷偶联剂处理后,改性不饱和聚酯。   熔融共混:将纳米无机粒子与聚合物基体在密炼机、双螺杆等混炼机械上熔融共混。如将PMMA和纳米SiO2粒子熔融共混后,双螺杆造粒制得纳米复合材料。又如利用偶联剂超声作用下处理纳米载银无机抗菌剂粒子,分散制得PP/抗菌剂、PET/抗菌剂、PA/抗菌剂等复合树脂,然后经熔融纺丝工艺加工成抗菌纤维。研究表明,将经过表面处理的纳米抗菌剂粒子通过双螺杆挤出机熔融混炼,在聚合物中可以达到纳米尺度分散,获得了具有良好综合性能的纳米抗菌纤维,对大肠杆菌、金黄色葡萄球菌的抗菌率达到95%以上(美国AATCC-100标准)。   机械共混:将偶联剂稀释后与碳纳米管混合,再与超高分子量聚乙烯(UHMWPE)混合放入三头研磨机中研磨两小时以上。将研磨混合物放入模具,热压,制得功能型纳米复合材料。   聚合法:利用纳米SiO2粒子填充(Poly(HEMA))制备了纳米复合材料。纳米SiO2粒子首先被羟乙基甲基丙烯酸(HEMA)功能化,然后与HEMA单体在悬浮体系中聚合。还有利用SiO2胶体表面带酸性,加入碱性单体4-乙烯基吡咯进行自由基聚合制得包覆型纳米复合材料。